Patent US10183786

Closure for a product-retaining container
[+] Show Details

US10183786

1. A cylindrical closure for a product-retaining container constructed for being inserted and securely retained in a portal-forming neck of said container, said closure comprising at least one thermoplastic polymer at least one natural organic filler, a plurality of cells, and a lateral surface, wherein the plurality of cells comprises a cell size in a range from 0.025 mm to 0.5 mm, and said closure comprises at least one of the following features (a) or (b): (24) (2)

(a) the lateral surface has a hardness in a range from 40 to 90 Shore A, according to ASTM D2240-10; and

(b) the lateral surface has a dynamic coefficient of friction in a range from 0.35 to 0.7, according to ASTM D1894-14.

2. The cylindrical closure according to claim 1, having a surface roughness Ra measured by contact profilometry in a range from 0.5 μm to 17 μm. (0)

3. The cylindrical closure according to claim 1, wherein said closure has an oxygen ingress rate of less than 3 mg oxygen per container in a first 100 days after being inserted and securely retained in the portal-forming neck of said container to close the container. (1) (0)

5. The cylindrical closure according to claim 1, having an overall density from 100 kg/m³to 800 kg/m³. (0)

6. The cylindrical closure according to claim 1, wherein the plurality of cells is a plurality of substantially closed cells. (0)

7. The cylindrical closure according to claim 1, wherein the plurality of cells comprises a cell size in a range from 0.05 mm to 0.35 mm. (0)

8. The cylindrical closure according to claim 1, wherein the at least one thermoplastic polymer is selected from the group consisting of polyethylenes, metallocene catalyst polyethylenes, polybutanes, polybutylenes, polyurethanes, silicones, vinyl-based resins, thermoplastic elastomers, polyesters, ethylenic acrylic copolymers, ethylene-vinyl-acetate copolymers, ethylene-methyl-acrylate copolymers, thermoplastic polyurethanes, thermoplastic olefins, thermoplastic vulcanizates, flexible polyolefins, fluorelastomers, fluoropolymers, polytetrafluoroethylenes, and blends thereof, ethylene-butyl-acrylate copolymers, ethylene-propylene-rubber, styrene butadiene rubber, styrene butadiene block copolymers, ethylene-ethyl-acrylic copolymers, ionomers, polypropylenes, and copolymers of polypropylene and copolymerizable ethylenically unsaturated comonomers, olefin copolymers, olefin block copolymers, cyclic olefin copolymers, styrene ethylene butadiene styrene block copolymers, styrene ethylene butylene styrene block copolymers, styrene ethylene butylene block copolymers, styrene butadiene styrene block copolymers, styrene butadiene block copolymers, styrene isoprene styrene block copolymers, styrene isobutylene block copolymers, styrene isoprene block copolymers, styrene ethylene propylene styrene block copolymers, styrene ethylene propylene block copolymers, polyvinylalcohol, polyvinylbutyral, polyhydroxyalkanoates, copolymers of hydroxyalkanoates and monomers of biodegradable polymers, poly(lactic acid), copolymers of lactic acid and monomers of biodegradable polymers, aliphatic copolyesters, aromatic-aliphatic copolyesters, and mixtures thereof. (0)

9. The cylindrical closure according to claim 1, wherein the at least one thermoplastic polymer is selected from the group consisting of polyvinylalcohol, polyvinylbutyral, polyhydroxyalkanoates, copolymers of hydroxyalkanoates and monomers of biodegradable polymers, poly(lactic acid), copolymers of lactic acid and monomers of biodegradable polymers, polycaprolactone, polyglycolide, poly(3-hydroxybutyrate), poly(3-hydroxybutyrate-co-3-hydroxyvalerate), poly(3-hydroxybutyrate-co-3-hydroxyhexanoate), poly(butylensuccinate) poly(butylensuccinate-co-adipate), poly(trimethyleneterephthalate), poly(butylenadipate-co-terephthalate), poly(butylensuccinate-co-terephthalate), poly(butylensebacate-co-terephthalate), lactic acid caprolactone lactic acid copolymers, lactic acid ethylene oxide lactic acid copolymers, and mixtures thereof. (0)

10. The cylindrical closure according to claim 1, wherein the at least one thermoplastic polymer is biodegradable according to ASTM D6400. (0)

11. The cylindrical closure according to claim 1, wherein the closure is produced by injection molding. (0)

12. The cylindrical closure according to claim 1, wherein the closure is produced by extrusion. (2) (0)

15. The cylindrical closure according to claim 1, wherein said closure comprises: (21) (3)

a. a core member comprising at least one thermoplastic polymer, and

b. at least one peripheral layer at least partially surrounding and intimately bonded to at least one surface of the core member, said at least one peripheral layer comprising at least one thermoplastic polymer,

wherein at least one of (i) the core member or (ii) the at least one peripheral layer comprises the plurality of cells.

16. The cylindrical closure according to claim 15, wherein the at least one natural organic filler is present in at least one of (i) the core member or (ii) the at least one peripheral layer. (0)

17. The cylindrical closure according to claim 15, wherein the at least one natural organic filler is present in the core member and in the at least one peripheral layer. (0)

18. The cylindrical closure according to claim 15, wherein the at least one natural organic filler is present in the core member. (0)

19. The cylindrical closure according to claim 15, wherein the at least one natural organic filler is present in the at least one peripheral layer. (0)

22. The cylindrical closure according to claim 15, wherein the at least one peripheral layer comprises natural organic filler particles with a particle size smaller than 500 μm. (0)

23. The cylindrical closure according to claim 15, wherein the core member comprises natural organic filler particles with a particle size in a range from 100 μm to 2000 μm. (0)

31. The cylindrical closure according to claim 15, wherein the closure is produced by a process comprising at least a process step of extrusion. (2) (0)

32. The cylindrical closure according to claim 15, wherein said core member and said at least one peripheral layer are extruded substantially simultaneously, or said core member is extruded separately to yield a pre-formed core member and subsequent thereto said at least one peripheral layer is formed in extrusion equipment peripherally surrounding and enveloping the pre-formed core member. (0)

34. The cylindrical closure according to claim 15, wherein the core member comprises a plurality of cells. (1) (0)

36. The cylindrical closure according to claim 15, wherein the core member comprises closed cells having at least one of an average cell size ranging from 0.02 mm to 0.50 mm or a cell density ranging from 8,000 cells/cm³to 25,000,000 cells/cm³. (0)

37. The cylindrical closure according to claim 15, wherein the at least one thermoplastic polymer of the core member and/or the at least one thermoplastic polymer of the at least one peripheral layer comprises a low density polymer having an unfoamed density in a range from 0.7 g/cm³to 1.5 g/cm³. (0)

38. The cylindrical closure according to claim 15, wherein the at least one thermoplastic polymer of the core member is selected from one of the following groups (a) or (b): (0) (2)

(a) the group consisting of polyethylenes, metallocene catalyst polyethylenes, polybutanes, polybutylenes, polyurethanes, silicones, vinyl-based resins, thermoplastic elastomers, polyesters, ethylenic acrylic copolymers, ethylene-vinyl-acetate copolymers, ethylene-methyl-acrylate copolymers, thermoplastic polyurethanes, thermoplastic olefins, thermoplastic vulcanizates, flexible polyolefins, fluorelastomers, fluoropolymers, polytetrafluoroethylenes, and blends thereof, ethylene-butyl-acrylate copolymers, ethylene-propylene-rubber, styrene butadiene rubber, styrene butadiene block copolymers, ethylene-ethyl-acrylic copolymers, ionomers, polypropylenes, and copolymers of polypropylene and copolymerizable ethylenically unsaturated comonomers, olefin copolymers, olefin block copolymers, cyclic olefin copolymers, styrene ethylene butadiene styrene block copolymers, styrene ethylene butylene styrene block copolymers, styrene ethylene butylene block copolymers, styrene butadiene styrene block copolymers, styrene butadiene block copolymers, styrene isoprene styrene block copolymers, styrene isobutylene block copolymers, styrene isoprene block copolymers, styrene ethylene propylene styrene block copolymers, styrene ethylene propylene block copolymers, polyvinylalcohol, polyvinylbutyral, polyhydroxyalkanoates, copolymers of hydroxyalkanoates and monomers of biodegradable polymers, poly(lactic acid), copolymers of lactic acid and monomers of biodegradable polymers, aliphatic copolyesters, aromatic-aliphatic copolyesters, and mixtures thereof; or

(b) the group consisting of polyvinylalcohol, polyvinylbutyral, polyhydroxyalkanoates, copolymers of hydroxyalkanoates and monomers of biodegradable polymers, poly(lactic acid), copolymers of lactic acid and monomers of biodegradable polymers, polycaprolactone, polyglycolide, poly(3-hydroxybutyrate), poly(3-hydroxybutyrate-co-3-hydroxyvalerate), poly(3-hydroxybutyrate-co-3-hydroxyhexanoate), poly(butylensuccinate) poly(butylensuccinate-co-adipate), poly(trimethyleneterephthalate), poly(butylenadipate-co-terephthalate), poly(butylensuccinate-co-terephthalate), poly(butylensebacate-co-terephthalate), lactic acid caprolactone lactic acid copolymers, lactic acid ethylene oxide lactic acid copolymers, and mixtures thereof.

39. The cylindrical closure according to claim 15, wherein the at least one thermoplastic polymer of the core member and/or the at least one thermoplastic polymer of the at least one peripheral layer is biodegradable according to ASTM D6400. (0)

40. The cylindrical closure according to claim 15, wherein the at least one thermoplastic polymer of the at least one peripheral layer is selected from the group consisting of polyethylenes, metallocene catalyst polyethylenes, polybutanes, polybutylenes, polyurethanes, silicones, vinyl-based resins, thermoplastic elastomers, polyesters, ethylenic acrylic copolymers, ethylene-vinyl-acetate copolymers, ethylene-methyl-acrylate copolymers, thermoplastic polyurethanes, thermoplastic olefins, thermoplastic vulcanizates, flexible polyolefins, fluorelastomers, fluoropolymers, polytetrafluoroethylenes, and blends thereof, ethylene-butyl-acrylate copolymers, ethylene-propylene-rubber, styrene butadiene rubber, styrene butadiene block copolymers, ethylene-ethyl-acrylic copolymers, ionomers, polypropylenes, and copolymers of polypropylene and copolymerizable ethylenically unsaturated comonomers, olefin copolymers, olefin block copolymers, styrene ethylene butadiene styrene block copolymers, styrene ethylene butylene styrene block copolymers, styrene ethylene butylene block copolymers, styrene butadiene styrene block copolymers, styrene butadiene block copolymers, styrene isoprene styrene block copolymers, styrene isobutylene block copolymers, styrene isoprene block copolymers, styrene ethylene propylene styrene block copolymers, styrene ethylene propylene block copolymers, polyvinylalcohol, polyvinylbutyral, polyhydroxyalkanoates, copolymers of hydroxyalkanoates and monomers of biodegradable polymers, aliphatic copolyesters, aromatic-aliphatic copolyesters, poly(lactic acid), copolymers of lactic acid and monomers of biodegradable polymers, polycaprolactone, polyglycolide, poly(3-hydroxybutyrate), poly(3-hydroxybutyrate-co-3-hydroxyvalerate), poly(3-hydroxybutyrate-co-3-hydroxyhexanoate), poly(butylensuccinate) poly(butylensuccinate-co-adipate), poly(trimethyleneterephthalate), poly(butylenadipate-co-terephthalate), poly(butylensuccinate-co-terephthalate), poly(butylensebacate-co-terephthalate), lactic acid caprolactone lactic acid copolymers, lactic acid ethylene oxide lactic acid copolymers, and combinations of two or more thereof. (0)

41. The cylindrical closure according to claim 15, wherein the at least one thermoplastic polymer present in the at least one peripheral layer is biodegradable according to ASTM D6400. (0)

42. The cylindrical closure according to claim 15, wherein the at least one peripheral layer comprises a thickness ranging from 0.05 mm to 5 mm. (0)

43. The cylindrical closure according to claim 15, wherein the at least one peripheral layer comprises a tough, score resistant, and mar resistant surface. (0)

44. The cylindrical closure according to claim 15, wherein the at least one peripheral layer comprises a density in a range from 300 kg/m³to 1500 kg/m³. (0)

51. The cylindrical closure according to claim 15, wherein the core member comprises at least one of an average cell size ranging from 0.05 mm to 0.1 mm or a cell density ranging from 1,000,000 cells/cm³to 8,000,000 cells/cm³. (0)

52. The cylindrical closure according to claim 15, wherein the at least one peripheral layer comprises a thickness ranging from 0.1 mm to 2 mm. (0)

53. The cylindrical closure according to claim 15, wherein the at least one peripheral layer comprises a density ranging from 750 kg/m³to 1100 kg/m³. (0)

20. The cylindrical closure according to claim 1, wherein the at least one natural organic filler is present in an amount in a range from 0.5 wt. % to 75 wt. %, based on a total weight of the closure. (0)

21. The cylindrical closure according to claim 1, wherein the at least one natural organic filler comprises particles having a particle size measured by a laser diffraction method according to ISO 13320 in a range from 0.1 μm to 2000 μm. (0)

24. The cylindrical closure according to claim 1, wherein the at least one natural organic filler has at least one of the following properties (a) or (b): (0) (2)

25. The cylindrical closure according to claim 1, wherein the at least one natural organic filler comprises a mixture of natural organic filler and a polymer. (0)

26. The cylindrical closure according to claim 1, wherein the at least one natural organic filler is at least partially coated with a polymer. (0)

27. The cylindrical closure according to claim 1, wherein the at least one natural organic filler is substantially free from oils and/or sensory constituents. (0)

28. The cylindrical closure according to claim 1, wherein the at least one natural organic filler comprises at least one ingredient selected from the group consisting of grape seed flour, grape skin powder, grape pomace flour, rice hull flour, oat hull flour, peanut hull flour, soybean hull flour, starch flour, corn starch flour, cellulose flour, microcrystalline cellulose, nanocellulose, wood flour, rice straw flour, corn cob flour, cricket flour, bagasse flour, kenaf flour, and hemp flour. (0)

29. The cylindrical closure according to claim 1, wherein the at least one natural organic filler comprises grape seed flour. (1) (0)

45. The cylindrical closure according to claim 1, being biodegradable according to ASTM D6400. (0)

46. A method of closing a container, the method comprising inserting the cylindrical closure according to claim 1 into the portal-forming neck of said container. (0)

47. The cylindrical closure according to claim 1 having an overall density from 150 kg/m³to 500 kg/m³. (0)

48. The cylindrical closure according to claim 1, wherein the at least one natural organic filler is comprised in an amount in a range from 10 wt. % to 70 wt. %, based on a total weight of the closure. (0)

49. The cylindrical closure according to claim 1, wherein the at least one natural organic filler comprises particles having a particle size measured by a laser diffraction method according to ISO 13320 in a range from 1 μm to 1000 μm. (0)

54. A method for producing a cylindrical closure, the method comprising the steps of (1) (6)

a. combining at least one natural organic filler with at least one thermoplastic polymer to obtain a polymer composition, wherein the at least one natural organic filler comprises at least one of the following features (i) or (ii): (i) the at least one natural organic filler comprises particles having a particle size measured by a laser diffraction method according to ISO 13320 in a range from 0.1 μm to 2000 μm, or

(ii) the at least one natural organic filler comprises at least one ingredient selected from the group consisting of grape seed flour, grape skin powder, grape pomace flour, rice hull flour, oat hull flour, peanut hull flour, soybean hull flour, starch flour, corn starch flour, cellulose flour, microcrystalline cellulose, nanocellulose, wood flour, rice straw flour, corn cob flour, cricket flour, bagasse flour, kenaf flour, and hemp flour;

b. adding at least one blowing agent to the polymer composition;

c. heating the polymer composition provided in step b. to obtain a heated composition;

d. introducing the heated composition into a mold;

e. forming the closure inside the mold; and

f. demolding the closure.

55. A closure produced according to the method according to claim 54. (0)

56. A method for producing a cylindrical closure comprising at least one thermoplastic polymer and at least one natural organic filler, said method comprising the steps of: (4) (6)

a. providing a core member composition comprising at least one thermoplastic polymer;

b. adding the at least one natural organic filler to the core member composition wherein the at least one natural organic filler comprises at least one of the following features (i) or (ii): (i) the at least one natural organic filler comprises particles having a particle size measured by a laser diffraction method according to ISO 13320 in a range from 0.1 μm to 2000 μm, or

c. adding at least one blowing agent to the core member composition;

d. heating the core member composition to obtain a heated composition;

e. extruding a continuous, elongated, substantially cylindrically shaped length of the heated composition to obtain, as a core member, a continuous elongated length of the core member composition having a cylindrical surface;

f. cutting the continuous elongated length of the core member composition obtained in method step e. in a plane substantially perpendicular to a central axis of said continuous elongated length to obtain the closure.

57. The method according to claim 56, further comprising maintaining an extrusion temperature in a range from 100° C. to 200° C. (0)

58. A closure produced according to the method according to claim 56. (0)

59. The method according to claim 56, further comprising a step of printing, coating, and/or post-treating the continuous elongated length of the core member composition obtained in method step e. (1) (0)

60. The method according to claim 56, further comprising maintaining an extrusion temperature in a range from 120° C. to 170° C. (0)

62. A method for producing a cylindrical closure comprising at least one thermoplastic polymer and at least one natural organic filler, said method comprising the steps of: (6) (7)

a. providing a core member composition comprising at least one thermoplastic polymer;

b. adding at least one blowing agent to the core member composition;

c. heating the core member composition to obtain a heated composition;

d. extruding a continuous, elongated, substantially cylindrically shaped length of the heated composition to obtain, as a core member, a continuous elongated length of the core member composition having a cylindrical surface;

e. providing a peripheral layer composition comprising at least one thermoplastic polymer;

f. extruding a separate and independent peripheral layer of the peripheral layer composition separately to, co-axially to and in intimate bonded engagement with the continuous, elongated length of the core member composition obtained in method step d., said separate and independent peripheral layer peripherally surrounding and substantially enveloping the cylindrical surface of the continuous, elongated length of the core member composition obtained in method step d. to obtain a multi-component elongated structure having a cylindrical surface; and

g. cutting the multi-component elongated structure obtained in method step f. in a plane substantially perpendicular to a central axis of said multi-component elongated structure to obtain the closure.

63. The method according to claim 62, further comprising the step of printing, coating, and/or post-treating the continuous elongated length of a core member composition obtained in method step d, or the closure obtained in method step g. (2) (0)

64. The method according to claim 62, wherein method steps d. and f. are conducted substantially simultaneously. (0)

66. The method according to claim 62, further comprising maintaining an extrusion temperature in a range from 100° C. to 200° C. (0)

67. The method according to claim 62, further comprising maintaining an extrusion temperature in a range from 120° C. to 170° C. (0)

68. A closure produced according to the method according to claim 62. (0)

70. The method according to claim 62, comprising at least one of the following steps: adding the at least one natural organic filler to the core member composition; or adding the at least one natural organic filler to the peripheral layer composition. (0)

View Abstract and Specification Size

PDF with Images and Document Face >

Full Text Publication >

Patent US10183786

Closure for a product-retaining container

Patent Matrix® Search